I have been looking around, but I have not seen it. Anyone know if you get a Biax cloth made with S2glass in a +/-45d ?
Why not E glass or carbon? Why not just cut S glass off the roll at 45*?
I know who can make it, but would require purchase of at least four rolls. Having a company make it will not be cheap.
Check out braider.com (A&P Braiders), we have gotten several things from them, and I am sure they have biax S.
else, a braid cut n half.
Eglass biax is available, but if I can pay more and get the the same cloth in sglass, I would. Not looking to have it custom made for me, but I would not write off buying one roll. Four would be overkill.
I was looking for something simliar to the knytex 1208/1708 with the stich mat on the back to get quick buildup. But I would like the entire cloth & mat to not contain Eglass (for added strength). If there are carbon alternatives that would work just as good I am definetly interested! But nothing I have seen yields the thickness buildup, as fast as the knytex.
The part I will be laying up is pretty large, so I will be fighting the clock to get the bag on, even with a ultra slow cure epoxy. For me to have to wetout 2 layers of sglass @45/45… when I could use one layer of knytex and get much faster buildup, would probably not work for me within the epoxy kick time. Just trying to speed up the layup process and gain strength if possible.
Thank you! I will check with them.